KA530F · Automotive glass bonding
KA530F Fast-Drying Glass Adhesive
Two-hour positioning at 23 °C with a 6.5 MPa cured tensile strength.
- Model
- KA530F
- Packs
- 310 ml · 400 / 600 ml · 200 L / 250 kg
- Tensile strength
- 6.5
- Elongation at break
- 450
What it is
One-component moisture-curing polyurethane with fast low-temperature cure, high initial adhesion and modulus, 2 h positioning, primerless on painted surfaces.
Specification
| Test | Standard | Typical value | Method |
|---|---|---|---|
| Appearance | — | Black homogeneous paste | — |
| Density (g/cm³) | 1.3±0.1 | 1.30 | GB/T 13477.2 |
| Sag resistance (mm) | ≤0.5 | 0 | GB/T 13477.6 |
| Skin time (min) | 10–30 | 15 | GB/T 13477.5 |
| Cure rate (mm/day) | ≥3.0 | 4.0 | HG/T 4363 |
| Volatile content (%) | ≤2 | 1 | GB/T 2793 |
| Shore A hardness | 55–65 | 58 | GB/T 531.1 |
| Tensile strength (MPa) | ≥6 | 6.5 | GB/T 528 |
| Elongation at break (%) | ≥400 | 450 | GB/T 528 |
| Tensile shear strength (MPa) | ≥4 | 4.5 | GB/T 7124 |
| Extrusion rate (ml/min) | ≥40 | 50 | GB/T 13477.4 |
Typical values from the printed catalogue, transcribed as printed. Where the catalogue printed a unit that does not fit the value (density in g/m³), the page shows g/cm³ — see the note below.
Catalogue notes.
- Density printed as g/m³; at 1.30 it should be g/cm³.
Packaging
| Format | Size | Carton / unit |
|---|---|---|
| cartridge | 310 ml | 12 / 20 / 24 pcs |
| sausage | 400 / 600 ml | 20 pcs |
| barrel | 200 L / 250 kg | — |
Where it is used
- Windscreen and side glass bonding on premium cars, buses and special vehicles
The rest of the family
Further reading
Windscreen adhesive: the specification guide — the guide this model belongs to
Ordering. Send the model, quantity, pack format and destination — we reply with
FOB/CIF pricing, lead time and the documents your customs broker will ask for.
Email a quote request or write to ryan@pu-karmind.net.